PRO-SET.
. HANDLING PROPERTIES
Technical Data Property Standard Units , 72 F (22 C). 77 F (25 C) | 85 F (29 C)
150g Pot Life | ASTM 02471 | minutes 430-561 342-418 | 236-290
– 4 500g Pot Life | ASTM D2471 | minutes 370-454 254-312 159-195
Viscosity Mixed | ASTMD2196. cP 898 584 396
| N F-251 – HT Viscosity (resin) __ ASTM D2196 cP 1433
Viscosity (hardener) | ASTM 02196 cP 121
HIGH TEMPERATURE INFUSION EPOXY ix ratio
COMBINED FEATURES Method Resin:Hardener| Resin:Hardener
_ ; . _ Weight 3.651 | 100:27.6
Low viscosity for rapid saturation of Weight Range 3.72:1-3.31:1 | 100:26.9-100:30.2
fiberglass, Kevlar and carbon fiber laminate Volume 3.001 100:333
with resin infusion and VARTM processes. Volume Range | 3.08:1-2.74:1 | 100:32.4-100:36.5
Extra slow cure speed hardener provides up DENSITY
to 12 hours of working time at 77 F (25 C). A 7
typical laminate will be gelled in about 16 to State Units 72 F (22 C)
20 hours at this temperature. Cured | Ibvgal (g/cc) | 9.42 (1.13)_
. oo. ce Resin Ib/gal (g/cc) _| 9.49 (1.14)
This combination is formulated specifically Hardener Ib/gal (g/cc) | 7.86 (0.94)
for resin infusion and VARTM processes. Do
not use in open mold applications. VISCOSITY VS TEMPERATURE
Elevated temperature cure is required; 1400
thermal and mechanical properties suitable 1200
for composite components and high- 4000
temperature tooling and molds. e
T, as high as 277 F (136 C) with proper post 2 800
cure providing excellent temperature stability g 600
and great part cosmetics. 2 400
Cost effective, high performance epoxy 200
formulation for synthetic composite 0
manufacturing. 50 60 670 )= 8010010120130
Quality-control tinting is available at no extra Temperature ( F)
charge; simply add “QC” after the product
Rev 5/ Dec 2015 code on your order.
Shelf life is 3 years for resin, 18 months for Test specimens were neat epoxy (without fiber reinforcement).
hardener when properly stored . Typical values, not to be construed as specification.