Able Industrial Products
Technical Data Sheet
AMTDMF50-01 Diluent 50
50 cps Silicone Fluid
PRODUCT DESCRIPTION
QM Diluent 50 is a low viscosity, polydimethlysiloxane fluid.
KEY FEATURES
+ Clear
+ Low viscosity
MAIN APPLICATIONS
+ Elastomer lubricant
+ Mold release agent
TYPICAL PROPERTIES
Che See eM Diluent S0stenr anes eres
Mix Ratio Varies as needed
Appearance Clear
Viscosity ~ 50 cps
Base Specific Gravity 0.96 0.97 .
APPLICATION
The applications for AMTDMF50, Diluent 50 are numerous and varied. All application methods
and recommended levels must be considered on an individual basis.
STORAGE AND SHELF LIFE
This product is best when used within 24 months from date of manufacture. See product label
and/or CoA for specific “Use By Date”.
Product should be stored in its original, unopened container in an environment that does not
exceed 38 C (100 F).
Storage beyond the date specified on the label does not necessarily mean that the product is no
longer usable. In this case, the properties required for the intended use should be checked for
quality assurance reasons.
DISCLAIMER
The technical data listed is provided for reference only and is not intended as product
specifications. For sales and technical assistance, please contact us at: (909) 930-1585.
For any questions or technical help, please call 909-030-1585
by | Sep 27, 2025
CHALLENGE 95 Page 1 of 1 Date: 05/18/2022
For more information call BJB Enterprises, Inc. (714) 734-8450 Fax (714) 734-8929
www.bjbenterprises.com
NON-WARRANTY “Except for a warranty that materials substantially comply with the data presented in Manufacturer’s latest bulletin describing the product (the basis for this substantial
compliance is to be determined by the standard quality control tests generally performed by Manufacturer), all materials are sold “AS IS” and without any warranty express or implied as to
merchantability, fitness for a particular purpose, patent, trademark or copyright infringement, or as to any other matter. In no event shall Manufacturer’s liability for damages exceed
Manufacturer’s sale price of the particular quantity with respect to which damages are claimed.”
PIGMENT, RELEASE & MISCELLANEOUS PRODUCT
Dedicated to QUALITY, SERVICE, SAFETY, and INNOVATION
CHALLENGE 95
A RELEASE DESIGNED FOR POLYURETHANE MOLDING
PRODUCT DESCRIPTION :
Challenge 95 is primarily a liquid release for flexible and rigid polyurethane elastomers and foams. It can be used for other polyurethane
systems as well, however, it is advisable to test prior to its use. Challenge 95 is a universal release for plaster, metal, urethane, and epoxy
molds.
Challenge 95 dries at room temperature to create a uniform film. This release is a blend of synthetic and natural high temperature
waxes dispersed in petroleum distillates.
APPLICATION INSTRUCTIONS :
Challenge 95 may be applied to hot or cold surfaces by spraying, wiping or brushing. Be sure to shake release containers prior to
use. New mold surfaces should be cleaned thoroughly and be treated with a mold release paste wax such as PartAll Hi-Temp for mold
break-in. Porous mold surfaces generally do require one or two release coats for every mold cycle. Release coats should be dry prior to
molding and drying speed can be gained by using forced air or infra-red heat. Challenge 95 can be polished to a high gloss after it has
dried or left alone to form a flat finish.
Mold cleaning may be required when residues buildup. Clean with a solution of detergent and water and dry thoroughly. If more
cutting action is required, use isopropyl alcohol alone or mixed into the detergent solution.
STORAGE AND HANDLING :
Store at 65-80 F (18-27 C) in a dry place. Unopened containers will have a shelf life of 12 months from date of shipment when
properly stored at room temperature. After use, reseal container and store in approved flammable storage cabinet or area. Do not
store in a refrigerator or cold room. Prior to using, blend thoroughly. Material should be above 65 F (18 C) when mixing.
SAFETY PRECAUTIONS:
Use in a well-ventilated area. Avoid contact with skin using protective gloves and protective clothing. Repeated or prolonged contact
on the skin may cause an allergic reaction. Eye protection is extremely important. Always use approved safety glasses or goggles
when handling this product.
IF CONTACT OCCURS :
Skin: Immediately wash with soap and water. Remove contaminated clothing and launder before reuse. It is not recommended
to remove resin from skin with solvents. Solvents only increase contact and dry skin. Remove contaminated clothing and
launder before reuse. Seek qualified medical attention if allergic reactions occur.
Eyes: Immediately flush with water for at least 15 minutes. Call a physician.
Ingestion: If swallowed, call a physician immediately. Remove stomach contents by gastric suction or induce vomiting only as
directed by medical personnel. Never give anything by mouth to an unconscious person. Contact a physician immediately.
Refer to the Material Safety Data Sheet before using this product.
WARNING: This product can expose you to chemicals including Toluene, which is known to the State of California to cause
cancer and birth defects or other reproductive harm. For more information, go to www.P65Warnings.ca.gov.
An ISO-9001 Certified company
by | Sep 27, 2025
Technical Data Sheet
AMT660P-01 High Performance Platinum Mold Making Silicone
AMT660P-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT660P-01 features: Medium viscosity, High durometer, High tear strength,
Minimal shrinkage
AMT660P-01 is supplied in matched kits with AMTCAT660P-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties
Base Catalyst
Color White Blue
Viscosity 53,000cps 3,300cps
Mixed Viscosity 30,000cps
Pot Life 60-90 minutes
Demold Time 8-12 hours
After Cure(7days@77F)
Tensile, PSI 970
Elongation, % 110
Durometer (shore A) 60
Tear (die B) min 130
Linear Shrinkage: % nil
Specific Gravity 1.1
by | Sep 27, 2025
i _ AEBS Industrial Products, inc.
Technical Data Sheet
AMTCAT292RED-03 High Performance RED Fast Catalyst
Description
AMTCAT292RED-03 is a RED Ultra Fast Curing agent for AMT292-01 Tin curing
base.
It Is mixed with AMT292-01 in a 10:1 base to catalyst ratio.
Typical Properties
Color Appearance: RED
Average Properties when Cured:
Appearance: Pink
Pot Life: 15-30 minutes
Tensile strength: 450psi
Tear Strength: 150pli
Elongation: 400%
Durometer, Shore A: 25-28
Applications: Hobby, Art projects, Foundry, Sculpture, Figurines, Candle, Soap
Molds, Special Effects, Rapid Prototyping, General Mold Making.
Storage and Handling Keep containers closed to prevent contamination and excess exposure to air and moisture. Store
in a cool, dry area, away from heat and sources of ignition. Refer to SDS for any hazards
DISCLAIMER This information is based on preliminary observation and has not been subjected to rigorous testing. The
above data is should not be used for specification writing. Suitability of this product for a specific application should be
determined under actual use conditions. No warranty, expressed or implied, is hereby made
2006 S. Baker Ave Ontario, Calif. 91761 (909)-930-1585 www.Able123.com
by | Sep 27, 2025
Technical Data Sheet
AMT595P-01 High Performance Platinum Mold Making Silicone
AMT595P-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT595P-01 features: Low viscosity, High durometer, High tear strength, Minimal
shrinkage
AMT595P-01 is supplied in matched kits with AMTCAT595P-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties Catalysts for AMT595-01
Base Cat AMTCATS95P-03 AMTCATS96P-03 AMTCATS97P-03
Color Translucent Clear Clear Clear
Viscosity 30,000cps 1,000cps 1,000cps 1,000
Mixed Viscosity 20,000cps 20,000 20,000 20,000
Pot Life 60-90 min 60-90min 60-90min 60-90min
After Cure(7days@77F)
Tensile, PSI 850 990 840
Elongation, % 570 675 725
Durometer (shore a) 25 20 15
Tear (die B) min 105 130 170
Linear Shrinkage: % nil nil nil
Specific Gravity 1.1 1.1 1.1
by | Sep 27, 2025
Technical Data Sheet
AMT242-01 Mold Making Silicone
AMT242-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT242-01 features: low viscosity, low durometer, high tear strength, resistance
to sulfur-based clays.
AMT242-01 is supplied in matched kits with AMTCAT242-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties
Base Catalyst
Color White Green
Viscosity 50,000cps 100cps
Mixed Viscosity 46,000cps
Pot Life 60-90 minutes
After Cure(7days@77F)
Tensile, PSI 500
Elongation, % 400
Durometer (shore A) 25
Tear (die B) min 130
Linear Shrinkage: % 0.3-0.4
Specific Gravity 1.16
by | Sep 27, 2025
Technical Data Sheet
AMT242-01 Mold Making Silicone
AMT242-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT242-01 features: low viscosity, low durometer, high tear strength, resistance
to sulfur-based clays.
AMT242-01 is supplied in matched kits with AMTCAT242-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties
Base Catalyst
Color White Green
Viscosity 50,000cps 100cps
Mixed Viscosity 46,000cps
Pot Life 60-90 minutes
After Cure(7days@77F)
Tensile, PSI 500
Elongation, % 400
Durometer (shore A) 25
Tear (die B) min 130
Linear Shrinkage: % 0.3-0.4
Specific Gravity 1.16
by | Sep 27, 2025
Technical Data Sheet
AMT242-01 Mold Making Silicone
AMT242-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT242-01 features: low viscosity, low durometer, high tear strength, resistance
to sulfur-based clays.
AMT242-01 is supplied in matched kits with AMTCAT242-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties
Base Catalyst
Color White Green
Viscosity 50,000cps 100cps
Mixed Viscosity 46,000cps
Pot Life 60-90 minutes
After Cure(7days@77F)
Tensile, PSI 500
Elongation, % 400
Durometer (shore A) 25
Tear (die B) min 130
Linear Shrinkage: % 0.3-0.4
Specific Gravity 1.16
by | Sep 27, 2025
Technical Data Sheet
AMT242-01 Mold Making Silicone
AMT242-01 is a room temperature curing silicone rubber compound designed for
the manufacture of flexible molds.
AMT242-01 features: low viscosity, low durometer, high tear strength, resistance
to sulfur-based clays.
AMT242-01 is supplied in matched kits with AMTCAT242-03 catalyst designed to
be used in a 10:1 ratio by weight.
Typical Properties
Base Catalyst
Color White Green
Viscosity 50,000cps 100cps
Mixed Viscosity 46,000cps
Pot Life 60-90 minutes
After Cure(7days@77F)
Tensile, PSI 500
Elongation, % 400
Durometer (shore A) 25
Tear (die B) min 130
Linear Shrinkage: % 0.3-0.4
Specific Gravity 1.16
by | Sep 27, 2025
5700 Skylab Road Phone: +1 714-899-8100 E-mail : airtech@airtechintl.com
y a lan Huntington Beach Fax: +1 714-899-8179 Website : www.airtechonline.com
INTERNATIONAL INC. CA 92647 USA
Data Sheet AIRPAC 15A &B
Fast curing two part silicone moulding putty
DESCRIPTION
Airpac 15 A & Bis a two component silicone putty that rapidly cures to give a resilient elastomer. The putty has
a 1:1 mix ratio and can be mixed mechanically or by hand without pre-weighing or degassing. Airpac 15 A&B
has good temperature resistance and is ideally suited for flexible tooling applications such as pressure pads,
mandrels, fillets and reproduction casts. Airpac 15 A & B can also be used as a shop-aid in vacuum bagging to fill
cavities, blend sharp corners and rapid fabrication of pressure intensifiers.
@ TECHNICAL DATA
Material type Uncured silicone rubber
Maximum use temperature 450 F (232 C)
Color Part A – White, Part B – Red
Hardness 50 Shore A
Elongation at break 225%
Mix ratio 1:1
Cure time (approximate) 15 minutes
Density 4.98 Ib/in (1.38 g/cm )
Shelf life 6 months from date of shipment when
stored in original packaging at 72 F (22 C)
@ SIZES
2 gallon (7.6 liter) Kit 10 Ibs (4.54 kg) 10 Ibs (4.54 kg)
10 gallon (37.8 liter Kit 50 Ibs (22.68 kg) 50 Ibs (22.68 kg)
M APPLICATION
Mixing instructions:
+ Measure out approximately equal amounts of part A and part B.
+ Blend the two components mechanically or by hand until a uniform color is obtained.
+ Apply mixed material and allow it to cure until rigid.
@ NOTES
+The maximum use temperature is dependent upon the duration at maximum temperature and is process
specific, Airtech recommends testing prior to use.
Last updated : 2020-11-23
Catalog position : Rubber
-Asthecondton or methods fuse, lncluing storage ae beyond our control Altech ternational nc does ot sme any responsi fe the performance of his material fo any parca ue. The mater ssld”s
Artech eration ne dclsne and buyer waive, any analimpled warantesincidg without mtn the pled warns of merchant and of ness fo pata use. The formation contaned heen
teptesents ypc properties and should nat be used for specication purposes Any tnsstio provide or yout convenience ony The afi anguages English andthe ofa law Calf, USA