. HANDLING PROPERTIES
Technical Data Property Standard Units 72 F (22 C)
150g Pot Life ASTM D2471 minutes 180
HTP 1 80 500g Pot Life ASTM D2471_| minutes 120
Viscosity Mixed ASTMD2196 | cP_ 00
HTP 280 Viscosity (resin) |_ASTM D2196 cP 2,500
Viscosity (hardener) | ASTM 02196 cP. 35
HIGH-TEMP INFUSION EPOXY MIX RATIO
COMBINED FEATURES Method Resin:Hardener Resin:Hardener
i 5 100:27.0
High-temperature, high-performance epoxy Weight 8.70:1 _ .
formulation for synthetic composite part and _Weight Range __| 3.80:1 – 3.50:1 | 100:26.3 – 100:28.5
tooling manufacture. _Volume | __3.00:1 100:33.3 _
Volume Range | 3.08:1 – 2.84:1 | 100:32.4 – 100:35.2
T, as high as 300 F (149 C) with proper post
cure. Provides excellent temperature stability DENSITY
and great part cosmetics. State Units 72 F (22 C)
Slow cure speed hardener provides 5 to 6 Cured |_Ib/gal (g/cc) tr 9.60 (1.15)
hours of working time at 72 F (22 C). A typical Resin__|_Ib/gal (g/cc) _|_ 9.69 (1.16)
laminate will gel in 10 to 12 hours at room Hardener Ib/gal (g/cc) | 7.85 (0.94)
temperature. VISCOSITY VS TEMPERATURE
This combination is specifically formulated T4400 ]
for resin infusion and VARTM processes. Not 40 ] mon | | 41. a a | =
for use in open mold applications. 1200 +} a t = |
Elevated temperature cure is required. 1000 | LN | _ | | |__iil
Parts can be pulled after 24-48 hours at room | | | | |
temperature or sooner after a mild initial cure > 800 18 oo on
of 90-110 F (32-43 C). See chart for post cure = | | | | |
information. 8 600 TT a el |
2 |
Quality-control tinting is available at no extra > 200 – | | | 1 ll
charge; simply add “QC” after the product | | | | |
code on your order. 200 | a a |
Shelf life is 3 years for resin and 18 months 0 + + { _r |__| = _| a ae
for hardener when properly stored?. 50 60 70 80 90 100 110 120 130
Rev 2 / Sept 2020 Temperature ( F) |
Typical values, nottobe consiruedas specification. = ~