81EHCCF2_TDS.pdf

e) RESINS.
Clear Casting System
Clear, Low Viscosity Liquid Epoxy Resin for
Casting, Potting, and Embedding
Pr CCR is a water-clear, UV stabilized, low-viscosity epoxy system designed
orview specifically for casting, potting, and embedding applications. Low color and
low viscosity allow for bubble-free, crystal clear casting ideal for art and
hobby applications. CCR is a USDA Certified BioPreferred Product with
30% biobased content
The CCR System features two hardener speeds: slow (CCS) for high build
casting resin applications and fast (CCF) for quick, small project fast casting
resin applications such as resin jewelry and more.
Tensile Modulus (ASTM D638) 448,000 psi (3.1 GPa) 440,850 psi (3.0 GPa)
Tensile Strength (ASTM D638) 8,140 psi (56.1 MPa) 7.910 psi (54.5 MPa)
Elongation (ASTM D638) 6% 65
Flexural Modulus (ASTM D790) 390,000 psi (2.7 GPa) 409,670 psi (2.8 GPa)
Flexural Strength (ASTM D790) 11,850 psi (81.7 (MPa) 11,100 psi (76.5 MPa)
Compression Strength (ASTM D695) 12,380 psi (85.4 MPa) 10,860 psi (74.9 MPa)
Tg Ultimate (OSC, midpoint) 129 F/51 C 127-F/SIC
Hardness (Shore D) 70-80 70-80
Mix Ratio (by volume) 21 21
Mix Ratio (by weight) 10:43 100.42
Viscosity (A/B/Mixed @ 77 F/25 O) 2160/30/370 2160/15/270
Component Density (specific density @ 77 F/25 C) 1.13 (resin), 0.98 (hardener) 1.13 (resin), 0.95 (hardener)
Mixed Density (specific density @ 77 F/25 C) 1.08 1.07
Pot Life (@ 77 F/25 C) 90 min 360 min
Tack Free Time (@ 95 F/35 C) 24 hrs 72 hrs
Recommended Full Cure 7 days @ 77 F/25 C, 7 days @ 77 F/25 C
Post cure recommended Post cure recommended
-NVIRONME! Al :
VOC Content (ASTM D2369) 0.08 Ibs/gal (9.2 g/L) 0.07 Ibs/gal (8.0 g/L)
Mixed Biobased Carbon Content (ASTM D6866) 20% 20%
This technical information is provided in good faith and is based on the best knowledge of Gougeon Brothers, Inc. We cannot guarantee this data
because conditions of product use are beyond our control.
TDS revised May 2020. Gougeon Brothers, Inc. 2020