23HP300-15_TDS.pdf

Adhesive Seton, ine CYANOACRYLATE ADHESIVE
ao REVISED: DECEMBER/2010
BLACK RUBBER TOUGHENED ADHESIVE
DESCRIPTION: What we bond:
The HP Series is a highly engineered rubber tough- ABS NBR
ened cyanoacrylate adhesive. it is elastomer modified Acrylic Neoprene
providing excellent impact resistance, thermocycling . Pr
properties, and heat aging properties. The TS Series Aluminum Nitrile
is ideal for bonding dissimilar surfaces that are Bakelite Nylon
exposed to high and low end temperatures. High end Brass Phenolic
temperature resistance up to 250 F. Chloroprene Polycarbonate
PHYSICAL PROPERTIES: Chrome Polyester
Color: Black Cooper Polystyrene
ecosity: ity: aia EPDM Porcelain
Bose iy ModifiedEthyl Fiberglass pvc
. Latex SBR
ubstrate ixture Time ond Streng
Steel < 12 Seconds > 2100 psi Natural Rubber Valox
Aluminum <12 Seconds > 1750 psi Wood
Neoprene <5 Seconds > 750 psi
ABS <10 Seconds > 900 psi CHEMICAL/SOLVENT RESISTANCE:
Pvc <5 Seconds > 900 psi % OF STRENGTH RETAINED AFTER AGING FOR 500 HOURS
Polycarbonate < 10 Seconds > 900 psi GASOLINE @ 22 C: 100%
Phenolic < 10 Seconds > 850 psi ISOPROPANOL @ 22 C: 100%
NOTE: Method used, ISO 4587, ETHANOL @ 22 C: 100%
Tensile Strength: FREON TA @ 22 C% 100%
Steel: > 1800 psi MOTOR OIL @ 40 C% 100%
NOTE: Method used, ISO 6922 POLYCARBONATE 40 C @ 95% RH 100%
ELECTRICAL PROPERTIES: DIRECTIONS FOR USE:
Dielectric Constant ASTM D 150 Dissipation Factor For optimum results parts should be clean and free from any
1 kHz 2 to 3.50/ < 0.02 contamination on the bonding surface. If parts do not mate flush together use a higher viscosity product to compensate for the Volume Resistivity ASTM D 257: 2 x 10 to 10 x 105 gap. Any excess adhesive can be removed using Remove Debonder. FACTORS AFFECTING CURE SPEED: GAP: Thin bond line results in faster cure speed. Larger STORAGE: gaps will lengthen cure speed. | Store product in unopened containers, out of direct sunlight, in HUMIDITY: Cure and fixture times can be influenced by a dry location. Material should be stored at or below 22 C. For the humidity conditions at the time of assembly. The extended shelf life unopened containers of the product may be higher the RH the faster cure and fixture times will be. refrigerated. Fixture time data based on our testing is conducted at 50% relative humidity. NON WARRANTY: information contained herein is based on test and information we believe to be reliable and accurate. It is offered in good faith for the benefit of the consumer. ASI shall not be liable for any injury, loss, or damage, in the use of it s chemical products since the conditions of us are beyond our control. In every case we urge and recommend the user conduct tests to determine to their own satisfaction that the product is of acceptable quality and suitable for their particular purpose under their own operating conditions. Statements concerning the possible use of our products are not intended as recommendations or to use our products in the infringement of any patent. These products are for Industrial Use only. Engineering Excellence For technical Information and support call 1-800-552-0299 or visit our website at .instantca.com